PLASCO DATA SHEET
SOQUEL, CA., 95073
TYPICAL PROPERTIES
831-464-1111       831-464-1100 (FAX)

 

MATERIAL:  TKP 003
GENERIC:  ABS/15%PTFE
 
 

ASTM TEST METHODS VALUE
SPECIFIC GRAVITY: D-792  g/cm3 1.14
WATER ABSORPTION: D-570  24hrs % 0.30
MOLD SHRINK FLOW: D-955  in/in .006
MOLD SHRINK TRANS: D-955  in/in .008
TENSILE STRENGTH: D-638   psi  6500
TENSILE ELONGATION: D-638  %
FLEXURAL STRENGTH: D-790  psi
FLEXURAL MODULUS: D-790   psi 375,000
COMPRESSIVE STRENGTH: D-695  psi
IZOD NOTCHED: D-256  ft-lb/in 2.0
IZOD UNNOTCHED: D-256   ft-lb/in
HARDNESS: D-785


CO. LINEAR THERM.EXP: D-696  10(-5) "/"F 5.2
THERMAL COND: C-177 btu-ft2/hr"F
DEFORMATION UNDER LOAD: D-621   %
HDT 66: D-648  F
HDT 264: D-648  F 200
FLAMMABILITY: UL  SUBJECT 94 HB


5 KV DECAY RATE: MIL-B-81705B
SURFACE RESISTIVITY: ohm/sq.
VOLUME RESISTIVITY: ohm-cm.


WEAR FACTOR: 10(-10)in3min/ft/lb/hr 300
STATIC FRICTION: 40psi 0.13
DYNAMIC FRICTION: 40psi  50fpm 0.16
LPV 10FPM: psi  fpm  18,000
LPV 100FPM: psi  fpm 4000


MELT TEMP: F 500
MOLD TEMP: F 200
CYLINDER TEMPS: F 400-560
DRYING TEMP: F 180
DRYING TIME: HRS 2-4

 
This information is based on our experience to date and we believe it to be reliable. It is intended only as a guide for use at your discretion & risk. We cannot guarantee favorable results and assume no liability in connection with its use. None of this information is to be taken as a license to operate under, or a recommendation to infringe, any patents. 