ASTM TEST
METHODS |
VALUE |
SPECIFIC GRAVITY: D-792 g/cm3 |
1.04 |
WATER ABSORPTION: D-570 24hrs % |
0.28 |
MOLD SHRINK FLOW: D-955 in/in |
.005 |
MOLD SHRINK TRANS: D-955 in/in |
.007 |
TENSILE STRENGTH: D-638
psi |
7500 |
TENSILE ELONGATION: D-638 % |
|
FLEXURAL STRENGTH: D-790 psi |
|
FLEXURAL MODULUS: D-790 psi |
390,000 |
COMPRESSIVE STRENGTH: D-695 psi |
|
IZOD NOTCHED: D-256 ft-lb/in |
3.0 |
IZOD UNNOTCHED: D-256 ft-lb/in |
|
HARDNESS: D-785 |
|
|
|
CO. LINEAR THERM.EXP: D-696 10(-5)
"/"F |
5.0 |
THERMAL COND: C-177 btu-ft2/hr"F |
|
DEFORMATION UNDER LOAD: D-621 % |
|
HDT 66: D-648 F |
|
HDT 264: D-648 F |
195 |
FLAMMABILITY: UL SUBJECT 94 |
HB |
|
|
5 KV DECAY RATE: MIL-B-81705B |
|
SURFACE RESISTIVITY: ohm/sq. |
|
VOLUME RESISTIVITY: ohm-cm. |
|
|
|
WEAR FACTOR: 10(-10)in3min/ft/lb/hr |
80 |
STATIC FRICTION: 40psi |
0.11 |
DYNAMIC FRICTION: 40psi 50fpm |
0.14 |
LPV 10FPM: psi fpm |
|
LPV 100FPM: psi fpm |
|
|
|
MELT TEMP: F |
500 |
MOLD TEMP: F |
200 |
CYLINDER TEMPS: F |
400-560 |
DRYING TEMP: F |
180 |
DRYING TIME: HRS |
|