PLASCO INC.

2829 SO. RODEO GULCH RD. #6
PLASCO DATA SHEET
SOQUEL, CA., 95073
TYPICAL PROPERTIES
831-464-1111       831-464-1100 (FAX)

 

MATERIAL:  TDF 603
GENERIC:  PPS/30%GF/15%PTFE
 
 

ASTM TEST METHODS VALUE
SPECIFIC GRAVITY: D-792  g/cm3 1.69
WATER ABSORPTION: D-570  24hrs % 0.02
MOLD SHRINK FLOW: D-955  in/in 0.003
MOLD SHRINK TRANS: D-955  in/in 0.009
TENSILE STRENGTH: D-638   psi  17500
TENSILE ELONGATION: D-638  % 1
FLEXURAL STRENGTH: D-790  psi 26500
FLEXURAL MODULUS: D-790   psi 1530000
COMPRESSIVE STRENGTH: D-695  psi 20000
IZOD NOTCHED: D-256  ft-lb/in 1.20
IZOD UNNOTCHED: D-256   ft-lb/in 8.0
HARDNESS: D-785 R122


CO. LINEAR THERM.EXP: D-696  10(-5) "/"F 1.3
THERMAL COND: C-177 btu-ft2/hr"F
DEFORMATION UNDER LOAD: D-621   %
HDT 66: D-648  F 510
HDT 264: D-648  F 500
FLAMMABILITY: UL  SUBJECT 94 V-0


5 KV DECAY RATE: MIL-B-81705B
SURFACE RESISTIVITY: ohm/sq.
VOLUME RESISTIVITY: ohm-cm. 10^16


WEAR FACTOR: 10(-10)in3min/ft/lb/hr 110
STATIC FRICTION: 40psi 0.15
DYNAMIC FRICTION: 40psi  50fpm 0.17
LPV 10FPM: psi  fpm  27000
LPV 100FPM: psi  fpm 35000


MELT TEMP: F 600
MOLD TEMP: F 250
CYLINDER TEMPS: F 500-675
DRYING TEMP: F 250
DRYING TIME: HRS 3
This information is based on our experience to date and we believe it to be reliable. It is intended only as a guide for use at your discretion & risk. We cannot guarantee favorable results and assume no liability in connection with its use. None of this information is to be taken as a license to operate under, or a recommendation to infringe, any patents.