ASTM TEST
METHODS |
VALUE |
SPECIFIC GRAVITY: D-792 g/cm3 |
1.45 |
WATER ABSORPTION: D-570 24hrs % |
0.08 |
MOLD SHRINK FLOW: D-955 in/in |
.0035 |
MOLD SHRINK TRANS: D-955 in/in |
.005 |
TENSILE STRENGTH: D-638
psi |
14,500 |
TENSILE ELONGATION: D-638 % |
|
FLEXURAL STRENGTH: D-790 psi |
|
FLEXURAL MODULUS: D-790 psi |
800,000 |
COMPRESSIVE STRENGTH: D-695 psi |
|
IZOD NOTCHED: D-256 ft-lb/in |
1.8 |
IZOD UNNOTCHED: D-256 ft-lb/in |
|
HARDNESS: D-785 |
R115 |
|
|
CO. LINEAR THERM.EXP: D-696 10(-5)
"/"F |
1.8 |
THERMAL COND: C-177 btu-ft2/hr"F |
|
DEFORMATION UNDER LOAD: D-621 % |
|
HDT 66: D-648 F |
|
HDT 264: D-648 F |
290 |
FLAMMABILITY: UL SUBJECT 94 |
V-1 |
|
|
5 KV DECAY RATE: MIL-B-81705B |
|
SURFACE RESISTIVITY: ohm/sq. |
10^16 |
VOLUME RESISTIVITY: ohm-cm. |
10^16 |
|
|
WEAR FACTOR: 10(-10)in3min/ft/lb/hr |
40 |
STATIC FRICTION: 40psi |
0.19 |
DYNAMIC FRICTION: 40psi 50fpm |
0.22 |
LPV 10FPM: psi fpm |
20,000 |
LPV 100FPM: psi fpm |
25,000 |
|
|
MELT TEMP: F |
600 |
MOLD TEMP: F |
250 |
CYLINDER TEMPS: F |
540-650 |
DRYING TEMP: F |
250 |
DRYING TIME: HRS |
3-4 |