| ASTM TEST
METHODS |
VALUE |
| SPECIFIC GRAVITY: D-792 g/cm3 |
1.22 |
| WATER ABSORPTION: D-570 24hrs % |
0.65 |
| MOLD SHRINK FLOW: D-955 in/in |
.0035 |
| MOLD SHRINK TRANS: D-955 in/in |
.0075 |
| TENSILE STRENGTH: D-638
psi |
22,000 |
| TENSILE ELONGATION: D-638 % |
4 |
| FLEXURAL STRENGTH: D-790 psi |
33,000 |
| FLEXURAL MODULUS: D-790 psi |
1,250,000 |
| COMPRESSIVE STRENGTH: D-695 psi |
|
| IZOD NOTCHED: D-256 ft-lb/in |
1.0 |
| IZOD UNNOTCHED: D-256 ft-lb/in |
6.5 |
| HARDNESS: D-785 |
|
|
|
| CO. LINEAR THERM.EXP: D-696 10(-5)
"/"F |
2 |
| THERMAL COND: C-177 btu-ft2/hr"F |
4 |
| DEFORMATION UNDER LOAD: D-621 % |
|
| HDT 66: D-648 F |
495 |
| HDT 264: D-648 F |
485 |
| FLAMMABILITY: UL SUBJECT 94 |
HB |
|
|
| 5 KV DECAY RATE: MIL-B-81705B |
<.3 |
|
| SURFACE RESISTIVITY: ohm/sq. |
10^04 |
| VOLUME RESISTIVITY: ohm-cm. |
10^04 |
|
|
| WEAR FACTOR: 10(-10)in3min/ft/lb/hr |
45 |
| STATIC FRICTION: 40psi |
0.15 |
| DYNAMIC FRICTION: 40psi 50fpm |
0.19 |
| LPV 10FPM: psi fpm |
12,000 |
| LPV 100FPM: psi fpm |
17,500 |
|
|
| MELT TEMP: F |
560 |
| MOLD TEMP: F |
225 |
| CYLINDER TEMPS: F |
500-575 |
| DRYING TEMP: F |
200 |
| DRYING TIME: HRS |
2-4 |