| ASTM TEST
METHODS |
VALUE |
| SPECIFIC GRAVITY: D-792 g/cm3 |
1.45 |
| WATER ABSORPTION: D-570 24hrs % |
.04 |
| MOLD SHRINK FLOW: D-955 in/in |
.0015 |
| MOLD SHRINK TRANS: D-955 in/in |
.0045 |
| TENSILE STRENGTH: D-638
psi |
27000 |
| TENSILE ELONGATION: D-638 % |
2.8 |
| FLEXURAL STRENGTH: D-790 psi |
36000 |
| FLEXURAL MODULUS: D-790 psi |
3100000 |
| COMPRESSIVE STRENGTH: D-695 psi |
|
| IZOD NOTCHED: D-256 ft-lb/in |
1.1 |
| IZOD UNNOTCHED: D-256 ft-lb/in |
8.8 |
| HARDNESS: D-785 |
|
|
|
| CO. LINEAR THERM.EXP: D-696 10(-5)
"/"F |
.6 |
| THERMAL COND: C-177 btu-ft2/hr"F |
5.2 |
| DEFORMATION UNDER LOAD: D-621 % |
|
| HDT 66: D-648 F |
510 |
| HDT 264: D-648 F |
505 |
| FLAMMABILITY: UL SUBJECT 94 |
V-0 |
|
|
| 5 KV DECAY RATE: MIL-B-81705B |
<.30 |
|
| SURFACE RESISTIVITY: ohm/sq. |
10^02 |
| VOLUME RESISTIVITY: ohm-cm. |
10^02 |
|
|
| WEAR FACTOR: 10(-10)in3min/ft/lb/hr |
160 |
| STATIC FRICTION: 40psi |
0.23 |
| DYNAMIC FRICTION: 40psi 50fpm |
0.20 |
| LPV 10FPM: psi fpm |
12000 |
| LPV 100FPM: psi fpm |
20000 |
|
|
| MELT TEMP: F |
600 |
| MOLD TEMP: F |
250 |
| CYLINDER TEMPS: F |
500-675 |
| DRYING TEMP: F |
250 |
| DRYING TIME: HRS |
3 |